E I DUPONT DE NEMOURS & CO INC
WILMINGTON, DE 19880
Material Dsg: 101(f2)+, 101F+, 101L+, E101(f1)+, E101L, 132F+, 133L+, 135F+
Description: Polyamide 66 (PA66) , designated "Zytel" furnished in the form of pellets.
Color Min. Thk.
mm Flame
Class
HWI
HAI RTI
Elec RTI
Imp RTI
Str
ALL 0.71 V-2 4 0 130 75 85
1.5 V-2 3 0 130 75 85
3.0 V-2 2 0 130 75 85
6.0 V-2 2 0 130 75 85
CTI: 0 HVTR: 0 D495: 6
(f1) - Suitable for outdoor use with respect to exposure to Ultraviolet Light, Water Exposure and Immersion in accordance with UL 746C.
(f2) - Subjected to one or more of the following tests: Ultraviolet Light, Water Exposure or Immersion in accordance with UL 746C, where the acceptability for outdoor use is to be determined by UL Inc.
+ - Virgin and Regrind from 1% to 50% by weight inclusive, have the same basic material characteristics.
NOTE - Material designations that are color pigmented may be followed by suffix letters and numbers.
Report Date: 07/29/1996 Underwriters Laboratories Inc ?/small> 324299-147
UL94 small-scale test data does not pertain to building materials, furnishings and related contents. UL 94 small-scale test data is intended solely for determining the flammability of plastic materials used in components and parts of end-product devices and appliances, where the acceptability of the combination is determined by ULI.
說明：
1. Color顏色：若為 ALL即表示所有顏色都合乎測試的規格
2. Min. Thk.mm：表示測試材質的厚度（單位mm）
3. Flame Class：表示防火等級，即材質經過以上測試條件，所得的數據予以分類並定義等級
4. RTI（RELATIVE TEMPERATURE INDEX）:相對溫度測試
RTI Elec（電氣性質相對溫度測試）：即受測試材質在運作狀態（即通電狀態）、環境測試溫度為130°C,材質壽命能達到測試標准
RTI Str（無機械性質相對溫度測試）：即受測試材質在沒有受到外力作用、環境測試溫度為110°C, 材質壽命能達到測試標准
RTI Imp（機械性質相對溫度測試）：即受測試材質在受到外力拖壓狀態、環境測試溫度為110°C, 材質壽命能達到測試標准
5. HWI (Hot Wire Ignition)熱線點火試驗：
受測試材質受電熱線加熱後，直到發火所須之時間（單位秒），時間愈長，等級愈高。
Mean Ignition Time(Sec) Assigned PLC
120≦IT 0 GOOD
BAD
60≦IT<120 1
30≦IT<60 2
15≦IT<30 3
7≦IT<15 4
0≦IT<7 5
6. HAI(Hight-Current Arc Ignition)高電流電弧點火試驗：
受測試材質受電弧加熱後，直到產生發火所需時間（單位秒），時間愈長，等級愈高。
Mean Number of Arc to Cause I nga Assigned PLC
120≦NA 0 GOOD
BAD
60≦NA<120 1
30≦NA<60 2
15≦NA<30 3
0≦NA<15 4
7. HVTR(High Voltage Arc Resistance to Ignition)高電壓電弧碳躋速率指數：
受測試材質在電壓上，單位時間測試材質試片在移動的電極棒下產生電弧碳化痕跡之距離。
Tracking Rate(mm/min) Assigned PLC
0<TR≦10 0 GOOD
BAD
10<TR≦25.4 1
25.4<TR≦80 2
80<TR≦150 3
150<TR 4
8. D495(材料高電壓、低電流、耐電弧)試驗：
將12500V電壓，逐步增加電流(10mA~40mA)之兩電極棒置於受測材質上，會在兩電極棒之間產生火花，並直到消失火花之時間。
Mean Time of Arc Resistance(Sec) Assigned PLC
420≦TAR 0 GOOD
BAD
360≦TAR<420 1
300≦TAR<360 2
240≦TAR<300 3
180≦TAR<240 4
120≦TAR<180 5
60≦TAR<120 6
0≦TAR<60 7
9. CTI(比較碳躋指數)試驗：
受測試材質試片置於電極棒下，以每30秒滴下0.1%之氯化氨(NH4CL)電解液一滴，能忍受滴電解液後才產生碳化痕跡（燃燒或電流突然放大）時之電壓數.
Tracking Darex(V) Assigned PLC
600≦TI 0 GOOD
BAD
400≦TI<600 1
250≦TI<400 2
175≦TI<250 3
100≦TI<175 4
0≦TI<100 5
10. “E I DUPONT DE NEMOURS & CO INC” 表示公司名稱和產地。
11. “E41938 ”表示黃卡認證號，一般與公司產地相對應的。
12. 其它注解略。